CONTENTS | %100 POLYESTER |
INNER TISSUE | POLYESTER |
WEIGHT | 525 g/m² ± %5 |
AIR PERMEABILITY | 11.000 – 14.000 lt/dm²/hour(Dp:200 Pa) |
THICKNESS | 2.0 mm |
TENSILE STRENGTH | Longitudinal: 150 kgf/5 cm - Transverse: 190 kgf/5 cm |
SURFACE TREATMENT | KALENDER AND GAZE PROCESS, WATER AND OIL REPELLENT HYDROPHOB IMPRESSION |
OPERATING TEMPERATURE | CONTINUOUS 150°C DRY TEMPERATURE |
ACID RESISTANCE | MIDDLE |
ALKALI STRENGTH | WEAK |
STRENGTH OF HYDROLYSIS | WEAK |
SOLVENT STRENGTH | EXCELLENT |
OXID STRENGTH | EXCELLENT |