CONTENTS | %100 Acrylic Homopolymer |
INNER TISSUE | ACRYLIC |
WEIGHT | 525 g/m² ± %5 |
AIR PERMEABILITY | 9.000 – 11.000 lt/dm²/hour (Dp:200 Pa) |
THICKNESS | 2.0 mm |
TENSILE STRENGTH | Longitudinal: 110 kgf/5 cm - Transverse: 140 kgf/5 cm |
SURFACE TREATMENT | KALENDER AND GAZE PROCESS |
OPERATING TEMPERATURE | CONTINUOUS 140°C DRY TEMPERATURE |
ACID RESISTANCE | MIDDLE |
ALKALI STRENGTH | MIDDLE |
STRENGTH OF HYDROLYSIS | EXCELLENT |
SOLVENT STRENGTH | GOOD |
OXID STRENGTH | GOOD |